Zinc Aluminium Metallized Capacitor Film for Capacitor Use

• Customization: Available
• Usage: Metallized Film for Capacitor Use
• Type: Metallized Film
• Model NO.: Metallized film
• Material: BOPP
• Feather: Capacitor Grade
• Hardness: Soft
• Transparency: Opaque
• Processing Type: Vacuum Coating
• Thickness: 2.0um-12um
• Width: 4.5mm-150mm
• Margin: 0.5mm/1.0mm/1.5mm/2.0mm/2.5mm/3mm/4mm/5mm
• Margin Types: Single Margin, Center Margin, Double Margin
• Normal Resistance: 2-4/6-9 Ohm/Sq
• Slitting: Straight Cut or Wave Cut
• ID(mm): 75+1/-0.5
• Od(mm): 180mm/200mm/220mm/240mm/280mm/320mm
• Types of Metallized: Al/Zn Metallized Film, Al Metallized Film
• MOQ: 10kgs
• Tensile Strength: >100 MPa
• Elongation Ar Break: 20-200%
• Heat Shrinkage: <5(120ºC, 10 Min)
• Density: 0.905+/-0.005
• Delivery Detail: 7-15 Days After Payment Confirmed
• Transport Package: Cartons
• Specification: BOPP film, thickness from 2um to 12um
• Trademark: CSF, Saifu
• Origin: Tongling
• Production Capacity: 3600 Ton/Year

Product Description

1.Basic information 
(1)Types Of Metallized Layer:Al Metallized Film , Zn/Al Metallized Film
(2)Width:4.5-130mm
(3)Thickness:2-12um
(4)Margin Value:0.5mm 1.0mm 1.5mm 2.0mm 2.5mm
(5)ID(mm):75
(6)OD(mm):180/240/270/320
(7)Processing Type:Vacuum Coating Capacitor Film
(8)Packaging Details :To be shipped in vaccum-sealed metallized plastic bags(9)Port :Shanghai Or Ningbo


2.Types of Metallized Layer





 

Base film	PP	PET
Normal thickness	2.0μm ~12.0μm	1.9μm ~12.0μm
Margin type	Single, two margins
Coating metal	Zinc-Aluminum alloy,Aluminum
Coating side	Single,two sides
Edge structure	Heavy edge
Cutting type	Straight cut, wave cut

3.Specifications of metallized film
(MPP Film):

Properties	Unit	Typical value
Density	g/cm^3	0.905±0.005
Thickness	µm	2.0 ~ 12
Tensile Strength	MD (MPa)	≥100
Elongation at Break	MD (%)	20~200
Elastic Modulus	MD (MPa)	2800
Heat Shrinkage	MD (%)	≤5 ( 120°C, 10min)
Wetting Tension	mN/m	38  (Corona treated side)
Surface Roughness	µm	0.08
Melting Point	ºC	172
Volume Resistivity	Ω.m	>10^15
Break-dowm Voltage	V/µm	≥350 ( 23°C, DC )
Dielectric Constant		2.2  (20ºC,1KHz)
Dissipation Factor		≤4×10^-4 (20ºC,1KHz )
RC	ΩF	≥5×10^4

(MPET Film):

Properties	Unit	Typical value
Density	g/cm^3	1.4
Thickness	µm	<5	5~12	≥12
Tensile Strength	MD (MPa)	≥84	≥108	≥120
Elongation at Break	MD (%)	≥22	≥33	≥44
Elastic Modulus	MD (MPa)	3500
Break-dowm Voltage	V/µm	≥200  ( 23°C, DC )	≥250  ( 23°C, DC )
Heat Shrinkage	MD (%)	≤2.5 ( 150°C, 10min)
Surface Roughness	µm	0.095
Melting Point	ºC	256
Volume Resistivity	Ω.m	>10^15   ( 23°C, Humidity 50%)
Dielectric Constant		3.2  (20ºC,1KHz)
Dissipation Factor	-	≤60×10^-4  (20ºC,1KHz )
RC	ΩF	≥1×10^4

4. WORKSHOP 

We have have 6 large-scale high vacuum coating equipment, 20 intellectualized slitting machines. 





5.Certificate 




6.Application





7.Packing
1)Film rolls are packed in plastic bags, vacuumed and put into desiccant for heat sealing.
2)The Bags are marked with type labels, mark thickness width, free margin width and resistance.
3)The bags are packed in carton cases.
4)The cartons are wrapped by wooden cases or reinforced carton.



8. Delivery 



Lead time: 7-15days after payment confirmed .



9. Question and answer 
1 .Q: Are you a manufacturer or a trading company?
A: We are a manufacturer located in Tongling  Anhui,Closed to Shanghai,NanJing. Welcome to visit our factory.

2.Q: What certificates do you have?
A:We strictly executive ISO9001 quality management system certification,and our products won CQC,TUV,UL,VDE and other performance certification,compliance with EU ROHS directive, with SGS report.

3 .Q: Can you provide free samples?
A:  Yes, we can. Free samples are available, but the postal fee should be paid by your side

            We will be at your service for  7*24 hours  !