Single Margin One Side Zn-Al Metallized Film for Capacitor Use

• Type: Metallized Film
• Material: BOPP
• Hardness: Soft
• Transparency: Opaque
• Thickness: 2.0um-12um
• Width: 4.5mm-150mm
• Model NO.: Metallized Film For Capacitor Use
• Margin: 0.5mm/1.0mm/1.5mm/2.0mm/2.5mm/3mm/4mm/5mm
• Margin Types: Single Margin, Center Margin, Double Margin
• Normal Resistance: 2-4/6-9 Ohm/Sq
• Slitting: Straight Cut or Wave Cut
• ID(mm): 75+1/-0.5
• Od(mm): 180mm/200mm/220mm/240mm/280mm/320mm
• Types of Metallized: Al/Zn Metallized Film, Al Metallized Film
• MOQ: 10kgs
• Tensile Strength: >100 MPa
• Elongation Ar Break: 20-200%
• Heat Shrinkage: <5(120ºC, 10 Min)
• Density: 0.905+/-0.005
• Delivery Detail: 7-15 Days After Payment Confirmed
• Transport Package: Cartons
• Specification: BOPP film, thickness from 2um to 12um
• Trademark: CSF, Saifu
• Origin: Tongling
• HS Code: 3920209090
• Production Capacity: 3600 Ton/Year

Product Description

Basic Information

Basic Information

(1)Types Of Metallized Layer:Al Metallized Film , Zn/Al Metallized Film
(2)Width:4.5-130mm
(3)Thickness:2-12um
(4)Margin Value:0.5mm 1.0mm 1.5mm 2.0mm 2.5mm
(5)ID(mm):75
(6)OD(mm):180/240/270/320
(7)Processing Type:Vacuum Coating Capacitor Film
(8)Packaging Details :To be shipped in vaccum-sealed metallized plastic bags
(9)Port :Shanghai Or Ningbo

 

Types of Metallized Layer

Type of Metallized Layer

 

Base film	PP	PET
Normal thickness	2.0μm ~15.0μm	1.9μm ~12.0μm
Margin type	Single, two margins
Coating metal	Zinc-Aluminum alloy,Aluminum
Coating side	Single,two sides
Edge structure	Heavy edge
Cutting type	Straight cut, wave cut

 

Specifications

MPP Film

Properties	Unit	Typical value
Density	g/cm^3	0.905±0.005
Thickness	µm	2.0 ~ 15
Tensile Strength	MD (MPa)	≥100
Elongation at Break	MD (%)	20~200
Elastic Modulus	MD (MPa)	2800
Heat Shrinkage	MD (%)	≤5 ( 120°C, 10min)
Wetting Tension	mN/m	38  (Corona treated side)
Surface Roughness	µm	0.08
Melting Point	ºC	172
Volume Resistivity	Ω.m	>10^15
Break-dowm Voltage	V/µm	≥350 ( 23°C, DC )
Dielectric Constant		2.2  (20ºC,1KHz)
Dissipation Factor		≤4×10^-4 (20ºC,1KHz )
RC	ΩF	≥5×10^4

 

MPET Film
 

Properties	Unit	Typical value
Density	g/cm^3	1.4
Thickness	µm	<5	5~12	≥12
Tensile Strength	MD (MPa)	≥84	≥108	≥120
Elongation at Break	MD (%)	≥22	≥33	≥44
Elastic Modulus	MD (MPa)	3500
Break-dowm Voltage	V/µm	≥200 ( 23°C, DC )	≥250 ( 23°C, DC )
Heat Shrinkage	MD (%)	≤2.5 ( 150°C, 10min)
Surface Roughness	µm	0.095
Melting Point	ºC	256
Volume Resistivity	Ω.m	>10^15 ( 23°C, Humidity 50%)
Dielectric Constant		3.2 (20ºC,1KHz)
Dissipation Factor	-	≤60×10^-4 (20ºC,1KHz )
RC	ΩF	≥1×10^4

 

Company Workshop

Company Workshop

We have have 6 large-scale high vacuum coating equipment, 20 intellectualized slitting machines. 

 

 

Certifications

Certifications 

 

 

Application

Application

 

 

Packaging

Packaging

1)Film rolls are packed in plastic bags, vacuumed and put into desiccant for heat sealing.
2)The Bags are marked with type labels, mark thickness width, free margin width and resistance.
3)The bags are packed in carton cases.
4)The cartons are wrapped by wooden cases or reinforced carton.

 

 

Delivery

Delivery

 

Lead time: 7-15days after payment confirmed .

All Right Reserved By Anhui Saifu Electronics Co., Ltd.

                                                                                                   

Anhui Saifu Electronics ©